Components Distribution in Positive Electrode in Lithium-ion Battery

リチウムイオン正極のラマンイメージング
▲Components distribution in positive electrode in Lithium-ion secondary Battery
: Lithium cobalt oxide
: Acetylene black
光源波长
532 nm
物镜
100倍 (NA=0.90)
光谱数目
48,000 (400×120)
测量时间
20分钟
 

Just 20 minutes imaging of components distribution on the surface of positive electrode

Above image shows an image of positive electrode in Lithium-ion battery analyzed by Raman microscopy. LiCoO2, which is active material, and acetylene black, which is conductive additive, are shown by red and blue image respectively. Within just 20 minutes, components distribution in wide area is obtained by Raman imaging with high-spatial resolution of the order of 350nm.


■Detail of the sample for the measurement
Mixture of LiCoO2, acetylene black and polyvinylidene fluoride with N-methylpyrrolidone are coated on both surfaces of alminum film and dried.

 

Observation of components distribution on positive electrode surfaces

Following graph shows averaged Raman spectrum in selected area, which is red and blue square in lower right hand picture, on observed Raman image. Spectrum in red square has 2 peaks of 485cm-1 and 597cm-1 related to LiCoO2. On the other hand, Spectrum in blue squqre has 2 peaks of 1350cm-1 and 1590cm-1 related to carbon.

Raman spectrum of positive electrode in Lithium-ion secondary battery
▲Averaged Raman spectrum in selected area, which are shown in red and blue square in lower right hand picture

 

Observation of components distribution on positive electrode surfaces after degradation

劣化後のリチウムイオン正極のラマンイメージング
▲Averaged Raman spectrum in selected area, which are shown in red and blue square in lower right hand picture
: Lithium cobalt oxide
: Acetylene black
: Cobalt oxide
光源波长
532 nm
物镜
100倍 (NA=0.90)
光谱数目
48,000 (400×120)
测量时间
20分钟
Above picture shows an image of positive electrode in Lithium-ion secondary battery degraded by laser light analyzed by Raman microscope under the same field of view as shown previous picture. With degradation of electrode, it is seen that LiCoO2 (red), acetylene black (blue) and cobalt oxide (green) are generated.

Following graph shows averaged Raman spectrum in selected area, which is red ,blue and green square in lower right hand picture, on observed Raman image. With degradation of electrode, it is seen that not only CoLiO2 (red) and carbon (blue) but also new components (green) which has several peaks in the reagion of lower wavenumber are generated. Focusing onto the Raman spectrum in the reagion of lower wavenumber, it is recognized that the spectrum selected in the green square has peaks of 482, 522 and 691cm-1 related to Co3O4.

劣化後のリチウムイオン正極のラマンスペクトル
低波数領域のラマンスペクトル
▲(Upper graph) Avaraged Raman spectrum in the selected area which are shown in red, blue and green square respectively
 (Lower graph)Expanded spectrum within lower wavenumber reagion of averaged Raman spectrum

Overlaid image with optical microscope image and raman image

透明度100% 透明度75% 透明度50% 透明度0%
Overlaid image with optical microscope image and raman image


RAMANtouch can show overlaid image with Raman image and optical microscope image after the measurements. The transparency of the Raman image can be changed as you wish by changing slider position from side to side on the software. As just described, RAMANtouch, which can image components distribution in the electrode materials within just 20 minutes, is a powerful tool for analyzing and evaluating of secondary battery materials.